Tensile properties of neutron irradiated solid-HIP 316(N): ITER Task T214, NET deliverable GB6 ECN-5
 
Auteur(s):
 
Gepubliceerd door: Publicatie datum:
ECN NUCLEAIR 1998
 
ECN publicatienummer: Publicatie type:
ECN-C--98-035 ECN rapport
 
Aantal pagina's: Volledige tekst:
22  Niet beschikbaar.

Samenvatting:
The tensile properties of neutron irradiated Hot Isostatically Pressed(HIP) joints of type 316L(N) stainless steel (heat PM-130) have been measured. Cylindrical tensile test specimens of 4 mm diameter were irradiated in the High Flux Reactor (HFR) in Petten, The Netherlands, simulating the first wall conditions by a combination of high displacement damage with proportional amounts of helium. The solid HIP specimens were irradiated up to a target dose level of 5 dpa at a temperature of 550K. The damage levels realized range from 3.0 to 4.1 dpa, with helium contents up to 38 appm. Post irradiation testing temperatures ranged from 300 to 700K. The report contains the experimental conditions and summarises the results, which are given in terms of engineering stresses and strains and reduction of area. The main conclusions are that the unirradiated solid-HIP material is very soft, assumingly due to the relatively large grain size. Neutron irradiation induces both hardening and reduction of ductility, similar to the behaviour of 316L(N) plate. No failures related to debonding were observed for the tests of the unirradiated samples, however one of eight tested irradiated specimens fractured in the HIP joint, showing a flat fracture surface and a low reduction of area. 6 refs.


Terug naar overzicht.