High temperature H2/CO2 separation using cobalt oxide silica membranes
 
Auteur(s):
Smart, S.; Vente, J.F.; Diniz da Costa, J.C.
 
Gepubliceerd door: Publicatie datum:
ECN Biomass & Energy Efficiency 28-8-2012
 
ECN publicatienummer: Publicatie type:
ECN-W--12-034 Artikel wetenschap tijdschrift
 
Aantal pagina's:
10  

Gepubliceerd in: International Journal of Hydrogen Energy (Elsevier), , 2012, Vol.37, p.12700 -12707.

Samenvatting:
In this work high quality cobalt oxide silica membranes were synthesized on alumina supports using a solegel, dip coating method. The membranes were subsequently connected into a steel module using a graphite based proprietary sealing method. The sealed membranes were tested for single gas permeance of He, H2, N2 and CO2 at temperatures up to 600 _C and feed pressures up to 600 kPa. Pressure tests confirmed that the sealing system was effective as no gas leaks were observed during testing. A H2 permeance of 1.9 _ 10_7- molm_2 s_1 Pa_1 was measured in conjunction with a H2/CO2 permselectivity of more than 1500, suggesting that the membranes had a very narrow pore size distribution and an average pore diameter of approximately 3 A┬░ . The high temperature testing demonstrated that the incorporation of cobalt oxide into the silica matrix produced a structure with a higher thermal stability, able to resist thermally induced densification up to at least 600 _C. Furthermore, the membranes were tested for H2/CO2 binary feed mixtures between 400 and 600 _C. At these conditions, the reverse of the water gas shift reaction occurred, inadvertently generating CO and water which increased as a function of CO2 feed concentration. The purity of H2 in the permeate stream significantly decreased for CO2 feed concentrations in excess of 50 vol%. However, the gas mixtures (H2, CO2, CO and water) had a more profound effect on the H2 permeate flow rates which significantly decreased, almost exponentially as the CO2 feed concentration increased.


Terug naar overzicht.